Standard methods used for processing these plates are bending, fl anging, cold roll forming, etc. Based on agreement these plates can be delivered in the condition suitable for hot-dip zinc-coating. These plates have excellent weldability because of low carbon equivalent.

Designation		Min. Yield Strength ReH [MPa]	Tensile Strength Rm [MPa]	Min. Elongation [%]	Min. Impact Energy KV 1) [°C/J] - longitudinal	Transverse Bend Test 2)	Dimension Table No.	Max. Thickness [mm]
S315MC		315	390-510	24	-20/40	0 t	table 3	20 3)
S355MC		355	430-550	23	-20/40	0.5 t	table 3	20 3)
S420MC		420	480-620	19	-20/40	0.5 t	table 3	20 3)
S460MC		460	520-670	17	-20/40	1 t	table 3	20 3)
S500MC		500	550-700	14	-20/40	1 t	table 3	16 3)
S550MC		550	600-760	14	-20/40	1.5 t	table 3	16 3)

Maximum value of the carbon equivalent as per the formula     on agreement
1) Testing on agreement
2) Minimum former diameter for 180° bend angle; t – plate thickness
3) Under standard

EQUIVALENT DESIGNATION